HOME    NICKEL & NICKEL ALLOY    Nimonic 90
Nimonic90 is an age-strengthened nickel-base wrentable superalloy that contains a large amount of cobalt and a variety of strengthening elements. The alloy has high tensile strength, creep resistance, good oxidation resistance and corrosion resistance at 815~870 ℃, and has high fatigue strength, good formability and weldability under repeated hot and cold alternation. Mainly supplies hot-rolled and cold-drawn bars, cold-rolled plates, strips and cold-drawn materials. Turbine disks, blades, high-

Nimonic 90

产品详情

Nimonic 90

Common Trade Names:UNS N07090,W.Nr2.4632

Nimonic90Chemical Composition:

Alloy

%

C

Cr

Ni

Ti

Fe

Cu

Mn

Si

Al

Co

90

Min.

18

Bal.

2.0

 

 

 

 

1.0

15.0

Max

0.13

21

3.0

1.5

0.2

1.0

1.0

2.0

21.0

Nimonic90Physical properties:

Density

8.18g/cm3

Melting point

1310-1370°C

Nimonic90minimum mechanical properties in the roomtemperature:

Alloy

Tensile strength

Yield Strength 0.2 % (MPa)

Elongation (%)

Hardness

HB

Rm N/mm2

Nimonic 90(solution)

1080 min

695 min

25 min
(0.45 mm-3.0mm)

243

Availability

Alloy 75 is available in Bar, Plate, Strip, Sheet, Wire,TubeRod, Forging Stock and Extruded Section. For all stock availability contactsales.

Specifications

Rod, Bar, Wire and Forging Stock

BS HR2, HR501, HR502 and HR503; SAE AMS 5829; AECMA PrEN 2295, 2296

2297, 2400, 2401, 2669 and 2670.

Plate, Sheet, Strip

BS HR202, AECMA PrEN 2298.

Pipe and Tube

BS HR402, AECMA PrEn 2299.

The recommended heat treatments for Nimonic 90 are as follows:

Nimonic 90 Bar

SolutionTreatment - 1080°C (1975 °F) for 8 hours + air cool or oil/ water quench

Precipitation Heat Treatment (As per BS HR2) - 700°C (1290 °F) for 16 hours + air cool

Nimonic 90 Sheet

Solution Treatment - 1100-1150°C for 1-10 minutes + air cool or oil /waterquench

Stabilization Heat Treatment - 925°C for 1 hour + air cool

Precipitation Heat Treatment - 750°C for 4 hours and air cool

(BS HR202/ MSRR 7016 / Siemens TLV 85252100 do not require the Stabilization Treatment stage)