Nickel 201
Nickel201
Similar Grades:
|
UNS |
Trademark |
W.Nr |
|
N02201 |
Nickel201 |
2.4060 |
Nickel 201Chemical Composition:
|
Grade |
% |
Ni |
Fe |
C |
Mn |
Si |
Cu |
S |
|
Nickel200 |
Min |
Bal. |
||||||
|
Max |
0.4 |
0.02 |
0.35 |
0.35 |
0.25 |
0.01 |
Nickel 201Physical Properties:
|
Density |
8.89g/cm3 |
|
Melting Point |
1440°C |
Nickel201The minimum value of the mechanical properties of an alloy at room temperature:
|
Form |
Status |
Tensile strength Rm N/mm² |
Yield strength Rp 0.2 N/mm² |
Elongation A5 % |
Brinell hardness HB |
|
Bar |
Hoe rolled |
60-85 |
15-45 |
35-55 |
45-80 |
|
Bar |
Cold drawing or annealing |
55-75 |
15-30 |
40-55 |
45-70 |
|
Plate |
Annealing |
55-80 |
15-40 |
40-60 |
45-75 |
|
Sheet |
Annealing |
55-75 |
15-30 |
40-55 |
70 max |
|
Tube |
Annealing |
55-75 |
12-30 |
40-60 |
70 max |
Nickel 201alloy has the following properties:
Pure commercial nickel with very low carbon content is approved for use in high temperature environments serving up to 1230°C.
Nickel 201 application:
Food processing and handling equipment, salt refining equipment.
Mining and marine mining.
Equipment required for the manufacture of industrial sodium hydroxide at temperatures above 300°C.
Production of organic or inorganic chlorides and fluorides: resistance to chlorine and fluorine gas corrosion
Nuclear reactors
Curved neck bottles and components in heat treatment furnaces, especially in carbonized and nitrided atmospheres
Catalytic regenerators in petrochemical production in applications above 700°C Alloy 600 is recommended for a long service life.